Looser Aluminium Bronze 75 (LAB 75) – CuAl10Ni5Fe4 DIN EN 12163/12167/12420
This wrought material is an aluminium multi-material bronze, which is available from stock in round, flat, square and hexagon full profile and as plates. Looser Aluminium Bronze 75 is a construction material with high strength properties, even at elevated temperatures; high permanent fatigue strength; good corrosion resistance against neutral and acidic, aqueous media as well as seawater; good resistance to scaling, erosion and cavitation.
The choice of alloys is made primarily according to the required strength properties. From this point of view, Looser Aluminium Bronze 78 and Looser Aluminium Bronze 79 have even higher values.
Hollow profiles from the same alloy group are primarily available from the continuous or centrifugal casting process in the form of tubes, cylinders or flange bushings under the trade name Looser Aluminium Bronze 75-1 and – with even higher mechanical properties – under Looser Aluminium Bronze 78-1. These two alloys are also available from stock in the form of round bars.
Chemical composition (DIN EN 12163:2016-11)
Element Cu Al Ni Fe Mn Zn Si Sn Pb Other
Min. [%] - 8,5 4 3 - - - - - -
Max. [%] Rest 11 6 5 1 0,4 0,2 0,1 0,05 0,2
Mechanical properties
Round bars
Flat bars
Hexagonal barsRange I DIN EN 12163:2016-11
Ø 8 – 70 mm
-
SW 10 – 70 mmRange II DIN EN 12163:2016-11
Ø 71 – 115 mm
-
-Range III DIN EN 12420:2014-09
Ø 122 – 403 mm
-
-Range IV DIN EN 12167:2016-11
-
Thickness 6 – 60 mm
-
Yield point Rp0,2 [N/mm2] ≥ 400 ≥ 320 ≥ 300 ≥ 320
Tensile strength Rm [N/mm2] ≥ 740 ≥ 680 ≥ 690 ≥ 680
Brinell hardness [HB] - - ≥ 195 -
Elongation at fracture A [%] ≥ 8 ≥ 10 ≥ 10 ≥ 10
Modulus of elasticity E [kN/mm2] ~ 120 ~ 120 ~ 120 ~ 120
Physical properties (Guideline values)
Coefficient of thermal expansion [10-6/K] 16 Electrical conductivity [m/Wmm2] 7
Thermal conductivity [W/mK] 51 Specific gravity [kg/dm3] 7.6
Standards
DIN EN 12163/12167 CuAl10Ni5Fe4 ASTM Alloy C 63000, C 63200
DIN 17665/17672 CuAl10Ni5Fe4 SAE CA 630
VSM 10802 CuAl10Fe5Ni5 BS 2033 CA 104
Material designation
DIN EN 12163 DIN 17665
Abbreviated designation Number Abbreviated designation Number
CuAl10Ni5Fe4 CW307G CuAl10Ni5Fe4 2.0966
Forms of delivery
Range [mm] Tolerance [mm] Manufacturing method
Round bars Ø 8 - 70 h11 drawn
Round bars Ø 71 - 115 0 / +2,2 pressed
Round bars Ø 122 - 403 0 / +1 forged and pre-turned
Square and flat bars 10 - 200 0 / +3 pressed, rolled or forged
Hexagonal bars 10 - 70 h12 pressed or drawn
Example uses
- Plain bearings with high threshold loads, highly stressed bearings in toggle presses, eccentric presses and forging machines.
- Suitable for plain bearings in hot operations due to high hot hardness.
- Guide bushings, pressure plates, sliding blocks, ball sockets, wear parts.
- Worm and gear wheels with very high loads up to medium speeds are a significant application.
- Pressure and spindle nuts, bolts, shafts, valve seat rings.
- Used in hydraulics as valve bodies, pistons, piston rods, seats, cones and control parts.
- Internal parts of high pressure fittings and hydraulic valves with the highest pressure levels, hot steam valves, fittings for high water velocities.
- Capacitor bottoms, jaws for resistance welding machines.
Machinability
Looser Aluminium Bronze 75 can be machined like steel with the same strength. Machinability, based on CuZn39Pb3 (Ms58Pb) is approximately 20%. Looser Aluminiumbronze is very suitable for forging (temperature range 850-975°C); but not for cold forming.
The annealing temperature range lies between 650-850°C; stress relief heat treatment takes place at 300-400°C. The melting point is 1035-1054°C.
In addition, this material can be welded in the argon arc welding process using electrodes of the same material and direct current. Not suitable for soft or hard soldering or for autogenous welding.
Sliding partners
Mating steel surfaces should be hardened and finely machined. The finer the sliding surfaces, the higher the expected service life. Good lubrication is essential.
Looser Aluminium Bronze 75 – Availability
- Over 150 sizes of tubular, round, flat, rectangular and hexagonal bars are available from stock or at short notice.
- Forged rings, bushings and edge profiles onto the base sizes or contour pre-fabricated.
- Sheets from 3-110 mm thickness and pre-cut parts are available at short notice.
- Ready-to-install parts in accordance with customer drawing.